Release agent # 1750A
Description
High-quality synthetic release agent carefully prepared by aluminum, magnesium and zinc die casting
Outstanding release force
The traditional working temperature is 205 ℃ ～ 310 ℃.
Outstanding release force
The traditional working temperature is 205 ℃ ～ 310 ℃.
Dilution
Aluminum alloy: initial ratio 1: 120 ~ normal ratio 1: 150
Magnesium alloy: initial ratio 1: 120 ~ normal ratio 1: 150
Zinc alloy: initial ratio 1: 120 ~ normal ratio 1: 150
Magnesium alloy: initial ratio 1: 120 ~ normal ratio 1: 150
Zinc alloy: initial ratio 1: 120 ~ normal ratio 1: 150
Feature
Forms a thin layer that is tough to resist sticking and promotes good metal flow.
The appearance of the casting is very bright and clean.
Does not cause paint and coating problems.
After dilution, the release agent in the central system or independent tank is very stable and does not deteriorate.
The appearance of the casting is very bright and clean.
Does not cause paint and coating problems.
After dilution, the release agent in the central system or independent tank is very stable and does not deteriorate.
Effect
Appearance: white
Taste: mild
Density: (1bs / gal) 8.2
PH: 8.8 ～ 9.2
Taste: mild
Density: (1bs / gal) 8.2
PH: 8.8 ～ 9.2
Chemical
High Temperature Polymer 45-55%
Modified Ester 5-10%
High Molecular Wt Alkane 10-15%
Non-ionic Emulsifiers 5-10%
Propylene Glycol 3-5%
Biocide 1%。
Modified Ester 5-10%
High Molecular Wt Alkane 10-15%
Non-ionic Emulsifiers 5-10%
Propylene Glycol 3-5%
Biocide 1%。