Coating Paste 6008LG#
Description
Coating Paste 6008LG# coating agent is a silver-white paste coating, suitable for aluminum, magnesium, copper, zinc and other alloys. It is mixed with inert metal refractory and a little graphite and a special high-temperature adhesive to prevent the adhesion of molten metal. painting agent. A protective film is formed on the surface of the metal tool and in the metal crucible.
The materials used in the coating are all high-purity special products. When in contact with molten metal, no impurities will be generated, and the molten metal will not be contaminated.
The materials used in the coating are all high-purity special products. When in contact with molten metal, no impurities will be generated, and the molten metal will not be contaminated.
Feature
When melting aluminum, magnesium, copper, zinc and other alloys, iron tools in contact with molten metal are often susceptible to corrosion by molten metal, resulting in a small amount of iron melting in the molten metal. When melting aluminum, it will seriously affect the strength and toughness of the alloy. In the case of copper and zinc alloys, the infiltration of iron will cause slag inclusion at hard spots to affect processing difficulties. Therefore, during the melting process, all iron tools in contact with molten metal, such as milling iron crucibles, and metal thermocouple protection Rods, ladles, scoops, covers, slag cakes, etc., must be coated with SK 6008 LG to isolate the contact between iron and molten metal. With high refractoriness and strong adhesion.
Effect
1. It has strong adhesion and is easy to use.
2. Conducive to cleaning tools and milling iron crucibles.
3. Extend the life of iron tools and milling crucibles.
4. Reduce the risk of contamination of molten metal.
2. Conducive to cleaning tools and milling iron crucibles.
3. Extend the life of iron tools and milling crucibles.
4. Reduce the risk of contamination of molten metal.
Chemical
SYNTHETIC POLYMERS 50-55 %
INERT MINERAL COMPONENT ( 30-35 %
GRAPHITE 10-20 %
INERT MINERAL COMPONENT ( 30-35 %
GRAPHITE 10-20 %
Pack
25KG/barrel
Other
1. Clean the tool first, and then apply SK 6008 LG to the surface of the tool with a brush, and then slowly put the tool in the aluminum broth and soak it for about ten seconds and pick it up immediately.
2. You can also put the iron tool to be painted on the side of the furnace to heat it, brush the coating agent on the surface of the tool, and then slowly immerse the tool in the aluminum broth, and take it out for about ten seconds before use.
3. There is no need to stop the machine during the production operation, and the coating agent can be applied to the small area where the tool falls off without affecting the work.
2. You can also put the iron tool to be painted on the side of the furnace to heat it, brush the coating agent on the surface of the tool, and then slowly immerse the tool in the aluminum broth, and take it out for about ten seconds before use.
3. There is no need to stop the machine during the production operation, and the coating agent can be applied to the small area where the tool falls off without affecting the work.